After sintered, MIM parts can be treated by machining、heat-treating、plating、E-coating etc. according to client’s requirements.Materials and Application Industry
|
Model
|
Materials
|
Application industry
|
|
Low-Alloy Steel
|
Fe-2Ni, Fe-8Ni
|
Structure Parts for car and mechanical
|
|
Stainless Steel
|
316L ,17-4PH
|
Medical and 3C
|
|
carbamide steel
|
WC-Co
|
Watches and cutter
|
|
W-Alloy
|
W-Ni-Fe, W-Ni-Cu, W-Cu
|
Military and communication industry
|
|
Ti-Alloy
|
Ti,Ti-6Al-4V
|
Medical and military structure parts
|
|
Magnetic
|
Fe,Fe 14 Nd 2 B,SmCo 5
|
Office auto-machine
|
Materials Properties
|
Material
|
Density
|
Hardness
|
Tensile strength
|
Elongation
|
|
g/cm 3
|
Rockwell
|
MPa
|
%
|
|
Low-Alloy
|
MIM-2200（After sintered）
|
7.65
|
45HRB
|
290
|
40
|
|
MIM-2700（After sintered）
|
7.65
|
69HRB
|
440
|
26
|
|
MIM-4605（After sintered）
|
7.62
|
62HRB
|
415
|
15
|
|
MIM-4605（Heat-treated）
|
7.62
|
48HRC
|
1655
|
2
|
|
Stainless Steel
|
MIM - 316L （After sintered）
|
7.92
|
67HB
|
520
|
50
|
|
MIM- 17-4PH （After sintered）
|
7.5
|
27HRC
|
900
|
6
|
|
MIM- 17-4PH （Heat-treated）
|
7.5
|
40HRC
|
1185
|
6
|
|
MIM - 430L （After sintered）
|
7.5
|
65HRB
|
415
|
25
|
|
W-alloy
|
95%W-Ni-Fe
|
18.1
|
30
|
960
|
25
|
|
97%W-Ni-Fe
|
18.5
|
33
|
940
|
15
|
|
Carbamide steel
|
YG8X
|
14.9
|
HRA90
|
2300
|
|
|
Tel：